Aim The objective of this study was to evaluate the effect of abrasion wear on surface roughness and microhardness of different commercially available resin composites simulating pH-challenges of the oral cavity. Methods Three resin composites (RC) were used in this study: one conventional: Z250; and two bulk fill resin composites (BRC): Tetric N-Ceram (TNC) and Sonic Fill (SF). The RC was inserted in a prefabricated mold (15mm wide x 4mm thickness) in two layers, or in a single layer for BRC. Thirty samples were prepared and surface roughness (Ra) and Knoop microhardness (KHN) test were performed at three different time-points of evaluation: baseline (24h after sample preparation); partial (after pH cycling); and final (after simulated toothbrushing procedure). Two samples of each group were selected after different treatments and analyzed descriptively on a scanning electron microscopy (SEM). Data from Ra and KHN were analyzed by two-way repeated-measures ANOVA and Bonferroni’s post-hoc test with a significance level set at 5%. Results Ra increased for all groups (p<0.001), at the final time-point, Z250 and TNC groups present the highest values. Oppositely, KHN decreased for all groups (p<0.001), Z250 group showed the highest KHN values for all time-points (p<0.001). The SEM imagens showed a regular surface for samples cycled and irregular with inorganic particles exposed for samples toothbrushed. Conclusion pH-cycling and simulated toothbrushing affected the superficial properties (roughness and Knoop microhardness), as observed at SEM imagens, with irregular surface with inorganic particles exposure.

Abstract: This in vitro study aimed to evaluate surface microhardness, roughness, color, gloss and topography of low-cost Brazilian resin composites, compared with an international one. All 120 samples (8mm ø x 2mm height) were prepared and divided into 5 groups: Ultrafill (Biodinâmica), Llis (FGM), Fill Magic (Coltene), Applic (Makira), and Filtek Z250XT (3M Oral Care). Surface microhardness (KHN) (n=10) was analyzed at two time periods: before and after simulated tooth brushing (STB). Other standardized samples of each group (n=10) were analyzed for surface roughness (Ra), color (ΔL, Δa, Δb, ΔE, ΔE00) and gloss unit (GU) at the same two periods. The topography of non-brushed and brushed samples of each group (n=4) was evaluated by scanning electron microscopy. Data were analyzed statistically by two-way repeated measures ANOVA with Bonferroni post-hoc test (KHN, Ra, GU), and one-way ANOVA with Tukey post-hoc test (ΔL, Δa, Δb, ΔE, ΔE00) (α=0.05). Topographic images were submitted to descriptive analysis. The low-cost Brazilian resin composites investigated were compared with the international one and revealed: lower KHN, regardless of before or after STB; statistically similar Ra before STB, except Ultrafill, which presented higher values; lower Ra after STB, except Ultrafill, which presented statistically similar values; statistically similar color change in ΔL, Δa, Δb parameters; statistically similar color change in ΔE, ΔE00 parameters, except Fill Magic, which presented lower values; lower gloss before STB; lower gloss after STB, except Ultrafill, which presented statistically similar values. In a situation of scarce resources, low-cost Brazilian composites might be an acceptable cost-effective restorative alternative.

Abstract: This study developed experimental gels containing titanium tetrafluoride (TiF4) combined with commercial 35% hydrogen peroxide (HP), and evaluated bleaching efficacy and pH of the gels, and mineral content and morphology of enamel submitted to these treatments. In phase-1, different stock gels mixed with TiF4 were combined with HP. In phase-2, the selected gels were tested on enamel/dentin specimens (n=8): HP; HP and Natrosol+TiF4 (HPnT); HP and Natrosol+Chemygel+TiF4 (HPncT); HP and Aristoflex+TiF4 (HPaT). Bleaching was performed in four sessions (3x15min-application/session). Color (CIEL*a*b*) and whiteness index (WID) were measured after each session, whereas whiteness index differences (ΔWID), color alteration (CIELab–ΔE, CIEDE2000-ΔE00), enamel morphology and pH, at end of bleaching therapy. The change in Knoop microhardness (ΔKHN) was compared before and after bleaching. Data were analyzed by two-way repeated measures ANOVA and Bonferroni (CIEL*, a*, b*), one-way ANOVA and Tukey (ΔWID, ΔE, ΔE00), and LSD (ΔKHN) tests (α=5%). SEM and pH measurements were submitted to descriptive analysis. No differences were observed in lightness (L*) or WID among the groups (p > 0.05), but HP exhibited lower b* values (p<0.05), higher ΔWID than HPnT, and the highest ΔE among the groups (p < 0.05). No differences in ΔE00 were observed between HP and HPncT (p > 0.05), and HPncT showed higher ΔKHN than HP (p < 0.05). HP presented pH values closer to neutral (6.9), whereas experimental agents showed acidic pH values (2.3–3.9). No morphological changes were observed in HP or HPncT groups. HPncT was able to bleach the enamel and maintain enamel microhardness and surface integrity, even at low pH.

O objetivo deste estudo foi avaliar a resistência adesiva por meio do teste de microtração (µTBS) entre dois substratos (esmalte e dentina) considerando dois fatores em estudo: Tipo de resina [metacrilato (Filtek Supreme) ou silorano (Filtek LS)] e tempo de envelhecimento (24 horas ou 3 meses). Vinte molares humanos foram selecionados e divididos em dois grupos (n=10) considerando dois substratos dentários, esmalte e dentina. O esmalte e a dentina de cada dente foram divididos em duas metades, por meio de uma lamínula. Cada dente foi restaurado usando ambas as resinas testadas, seguindo instruções do fabricante. As amostras foram seccionadas, resultando em quatro palitos para cada tipo de resina. Metade dos palitos foi testada após 24h e o restante após três meses. O ensaio de microtração (µTBS) foi conduzido numa velocidade de 0,05 mm/s. Os dados foram analisados usando three-way ANOVA e teste de Tukey HSD (α= 0,05). Diferença significante foi encontrada para o fator resina e substratos (p<0,05), porém não houve influência do tempo de envelhecimento e interações entre fatores estudados. A resina à base de metacrilato apresentou maior resistência adesiva do que a silorano. A adesão em esmalte foi significativamente maior do que em dentina, independente da resina e do tempo de envelhecimento. Três meses de armazenamento não foram suficientes para causar degradação da interação adesiva, para ambas as resinas compostas, no esmalte e na dentina.

The aim of this study was to evaluate the microtensile bond strength (µTBS) of two substrates (enamel and dentin) considering two study factors: type of composite resin [methacrylate-based (Filtek Supreme) or silorane-based (Filtek LS)] and aging time (24 h or 3 months). Twenty human molars were selected and divided into 2 groups (n=10) considering two dental substrates, enamel or dentin. The enamel and dentin of each tooth was divided into two halves separated by a glass plate. Each tooth was restored using both tested composite resins following the manufacturer's instructions. The samples were sectioned, producing 4 sticks for each composite resin. Half of them were tested after 24 h and half after 3 months. µTBS testing was carried out at 0.05 mm/s. Data were analyzed by three-way ANOVA and Tukey's HSD tests at α=0.05. Significant differences between composite resins and substrates were found (p<0.05), but no statistically significant difference was found for aging time and interactions among study factors. The methacrylate-based resin showed higher µTBS than the silorane-based resin. The µTBS for enamel was significantly higher than for dentin, irrespective of the composite resin and storage time. Three months of storage was not sufficient time to cause degradation of the bonding interaction of either of the composite resins to enamel and dentin.

As cerâmicas dentais são conhecidas pela excelência em reproduzir artificialmente dentes naturais. Recentemente, devido ao aprimoramento da tecnologia cerâmica, surgiram as restaurações livres de metal. Entretanto, as tradicionais metalocerâmicas ainda preenchem adequadamente os requisitos de alta resistência, longa sobrevida em meio bucal e estética favorável. Neste contexto, é fundamental conhecer a especificidade de cada sistema cerâmico a fim de indicá-lo adequadamente às diversas situações clínicas. Este artigo relata um caso de reabilitação integral e integrada de paciente de 50 anos de idade, portador de espaços edêntulos, restaurações protéticas posteriores e restaurações diretas anteriores insatisfatórias, resultando em comprometimento da qualidade de vida nos âmbitos funcional e psicossocial, utilizando coroas metalocerâmicas. O impacto na qualidade de vida foi mensurado utilizando um instrumento genérico, OHIP-14, validado pela Organização Mundial de Saúde, que abrange tanto a dimensão biológica, como a dimensão psicossocial. Este instrumento foi aplicado à paciente antes e após o tratamento, obtendo pontuação total de 28 e 0 respectivamente, o que mostra que a condição de saúde oral representa fator de grande impacto sobre a qualidade de vida. A reabilitação oral proporcionou restabelecimento funcional e estético, harmonia do sistema estomatognático e melhoria da qualidade de vida da paciente

Dental ceramics present excellent ability to reproduce the natural teeth regarding esthetic and biomechanics. Recently, due to the advancement of ceramic technology, metal-free restorations were developed. However, the traditional metal-ceramic restorations still present the requirements of high strength, long survival in the oral environment and favorable aesthetics. In this context, it is essential to know the specificity of each ceramic system available in order to apply it properly to various clinical situations. This report describes an integrated rehabilitation using metal-ceramic restorations of a patient at 50 years of age, who presented edentulous spaces, and previous unsatisfactory composite and amalgam restorations, and indirect metallic restorations, leading to compromised quality of life in both functional and psychosocial aspects. The impact on quality of life was measured using a generic instrument, OHIP-14, validated for the World Health Organization, which covers both the biological and the psychosocial dimensions. This instrument was applied to the patient before and after treatment. The patient had an overall OHIP-14 score of 28 before the treatment and after treatment the score decreased to 0, showing that dental and oral health conditions are factors that do impact on the quality of life. Rehabilitation has provided functional and aesthetic restorations, harmony of the stomatognathic system and improvement of life quality.

One of the clinically relevant problems dentists face when restoring endodontically treated teeth is the mismatch between fiber post and post space diameters, which results in an excessively thick resin cement layer. Fiber post relining appears as a solution for this problem. OBJECTIVES: The aim of this study was to evaluate the effect of fiber post relining with composite resin on push-out bond strength. MATERIAL AND METHODS: Twenty bovine incisors were selected to assess post retention. The crowns were removed below the cementoenamel junction and the root canals were treated endodontically and flared with diamond burs. The roots were allocated into two groups (n=10): G1: fiber posts without relining and G2: fiber posts relined with composite resin. The posts were cemented with a dual-cured resin cement and the specimens were sectioned transversally. Three 1.5-mm thick slabs were obtained per root and identified as cervical, medium and apical thirds. The push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. The failure mode of fractured specimens was analyzed under scanning electron microscopy. Data were analyzed by split-plot ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. RESULTS: Relined fiber posts presented higher retention values than non-relined post in all thirds. No statistically significant differences (p>0.05) were found among thirds for relined posts. All failures occurred at the interface between resin cement and root dentin. CONCLUSIONS: Relining with composite resin seems to be an effective method to improve the retention of fiber posts to flared root canals.

Este estudo determinou a resistência e o tipo de fratura do esmalte suportado pelos materiais restauradores ionômeros de vidro convencional e modificado por resina e resina composta, bem como a influência dessa técnica restauradora na resistência das cúspides dos dentes. A remoção da estrutura dental para o preparo de cavidades tipo classe II e a presença de esmalte socavado diminuiram significativamente a resistência das cúspides dos dentes em relação ao dente hígido (p < 0,01). Os materiais restauradores usados como suporte de esmalte reduziram o índice de fratura das cúspides restauradas, mas não aumentaram estatisticamente os valores de resistência à fratura. Todos os grupos experimentais apresentaram modificações no padrão de fratura

This study determined the resistance to fracture and its pattern for enamel supported with conventional and modified glass ionomer cements, and composite resin restorative materials, as well as the influence of these restorative techniques on cuspal strength of teeth. Removal of dental structure by class II cavity preparations and unsupported enamel had decreased significantly the cuspal strength in relation to healthy teeth (p < 0.01). Restorative materials used to support enamel reduced the fracture rate of restored cusps, but did not increase the fracture resistance values statistically. All tested groups presented alterations in the fracture pattern